Figure 5

Photothermal heating curves of MoS₂-modified akermanite (MS-AKT) scaffolds with different sizes (diameter: 6.0 mm, 8.5 mm, 11.0 mm) at dry (a) and wet (b) environment under 808-nm laser irradiation at the power density of 0.50 W cm⁻²; Photothermal heating curves of MS-AKT scaffolds (diameter: 8.5 mm) at different laser power density (0.2, 0.3, 0.4, 0.5 and 0.6 W cm⁻²) at dry (c) and wet (d) environment; Photothermal heating curves of MS-AKT scaffolds with different contents of MoS₂ at dry (e) and wet (f) environment (808 nm, 0.5 W cm⁻²). The final temperature of MS-AKT scaffolds could be well modulated by altering the scaffold sizes, laser power densities and MoS₂ contents.