Figure 3
From: Effect of liner and porcelain application on zirconia surface structure and composition
After the treatments specified in Figure 1 were complete, the composition of zirconium, oxygen, and yttrium for different groups as determined by EDS in weight percent. For zirconium, there was a statistical difference (P<0.05) in the composition between Group Mill-Sin and Group Ly-HF, Group HF and Group Ly-HF, Group Lin-Ly-HF and Group Ag, Group Lin-Prs-HF and Group Ly-HF, Group Lin-Ly-HF and Group Ag, Group Ly-HF and Group Ag. For oxygen, there was a statistical difference (P<0.05) in the composition between Group HF and Group Ly-HF, Group Lin-Ly-HF and Group Ag, Group Ly-HF and Group Ag. For yttrium, there was a statistical difference (P<0.05) in the composition between Group Lin-HF and Group Lin-Ag-HF, Group Lin-HF and Group Prs-Ag-HF, Group Lin-Ag-HF and Group Ly-HF, Group Lin-Ag-HF and Group Ly-Ag-HF, Group Ly-HF and Group Lin-Prs-Ag-HF, Group Ly-HF and Group Prs-Ag-HF, Group Ly-Ag-HF and Group Prs-Ag-HF. EDS, energy dispersive spectroscopy.