Table 1 Summary of effective g-factors and diamagnetic shifts in monolayer TMDs.

From: Exciton diamagnetic shifts and valley Zeeman effects in monolayer WS2 and MoS2 to 65 Tesla

Material

A exciton g-factor

B exciton g-factor

σA (μeV T−2)

σB (μeV T−2)

Monolayer WS2

−3.94±0.04

 

0.32±0.02

 
 

−3.33±0.04 (bulk)

−3.99±0.04

0.64±0.02 (bulk)

0.11±0.02

 

−3.2±0.3 (bulk)53

   

Monolayer MoS2

−4.0±0.2

   
 

−4.6±0.08 (bulk)55

−4.65±0.17

—

—

 

−3.1±0.1 (bulk)53

   

Monolayer WSe2

−3.7±0.2 (ref. 16)

—

—

—

 

−4.37±0.15 (ref. 13)

   
 

−1.57 to −2.86 (ref. 14)

   
 

−4±0.5 (ref. 17)

   

Monolayer MoSe2

−3.8±0.2 (refs 12, 16)

—

—

 
 

−4.1±0.2 (ref. 15)

   
  1. Experimentally measured exciton g-factors corresponding to the valley Zeeman effect, and diamagnetic shift coefficients σ, in monolayer transition-metal dichalcogenide materials. Measurements from this work are indicated in boldface. For comparison, also included are selected measurements from bulk crystals.
Back to article page