Figure 5: Li1.2Ti0.4Mn0.4O2 with a cation disordered rocksalt structure. | Nature Communications

Figure 5: Li1.2Ti0.4Mn0.4O2 with a cation disordered rocksalt structure.

From: Origin of stabilization and destabilization in solid-state redox reaction of oxide ions for lithium-ion batteries

Figure 5

(a) Neutron diffraction pattern of the as-prepared sample; (b) charge/discharge curves in a Li cell at a rate of 5 mA g−1 at 50 °C; (c) discharge capacity retention and an SEM image of the ball-milled sample and (d) changes in O K-edge and Mn LII, III-edge XAS spectra on charge in Li cells. The samples used in (d) were prepared at 50 °C in Li cells.