Figure 2: Magnetotransport properties of (Nd1−xPrx)2Ir2O7 at several pressures.
From: Magnetic-field induced multiple topological phases in pyrochlore iridates with Mott criticality
Magnetic field dependence of resistivity (a–e) and Hall conductivity (f–j) for a field along the [001] crystallographic direction at (a,f) 1.0 GPa, (b,g) 1.4 GPa, (c,h) 1.8 GPa, (d,i) 2.2 GPa and (e,j) 3.3 GPa (x=0.5), respectively. Magnetic field dependence of resistivity (k–o) and Hall conductivity (p–t) for a field along [111] direction at (k,p) 1.0 GPa, (l,q) 1.4 GPa, (m,r) 1.8 GPa, (n,s) 2.2 GPa and (o,t) 3.3 GPa (x=0.5), respectively. The solid (broken) lines are the resistivity on increasing (decreasing) field process which is indicated by black arrows.