Figure 2: Structural evolvement as a function of fs.
From: Rapid fabrication of hierarchically structured supramolecular nanocomposite thin films in one minute
Cross-sectional TEM images of a ∼220-nm thin film of a blend of PS(19 kDa)-b-P4VP(5.6 kDa)(PDP)1.7 and 6 vol% of ∼5 nm Au nanoparticles that was solvent annealed under chloroform vapour at different fs. The film thickness profile during solvent annealing is shown in a. The film was characterized at fs=(b) 0, (c) 0.13, (d) 0.23 and (e) 0.31, respectively. Scale bar=100 nm.