Abstract
Dielectric relaxation measurements and 13C NMR measurements were carried out on an amorphous network polymer derived from poly[2-(2-methoxyethoxy)ethyl glycidyl ether]triol with 2,4-toluenediisocyanate. The main relaxation and the higher frequency relaxation were observed in the dielectric spectra. The main relaxation was found to be symmetrical and broad with a half width of 5 decades in a frequency domain. The higher frequency process is considered to be the γ process of ethylene oxide chains due to the local twisting mode. The temperature dependence of T1 and T1ρ of the ethylene oxide carbon showed minima and it is clearly shown that the relaxation times obtained from the dielectric measurements correspond to the relaxation time obtained from the T1ρ measurements of the ethylene oxide carbon. The temperature dependence of T1 was well described assuming the Cole-Cole spectral density function with the shape factor β obtained for the dielectric main relaxation. The 13C magnetization decay of the ethylene oxide carbon in the rotating frame was found to be given by two components (slow and fast components) below the relaxation temperature. The broad dielectric relaxation and the decay profiles of the ethylene oxide carbon are discussed in terms of the branched structure of the network.
Similar content being viewed by others
Log in or create a free account to read this content
Gain free access to this article, as well as selected content from this journal and more on nature.com
or
References
J. R. MacCallum and C. C. Vincent Ed., “Polymer Electrolyte Reviews-1”, Elsevier, Amsterdam, 1987.
M. Watanabe, in “Solid State Ionics, Material and Application,” B. V. R. Chowdari, S. Chandra, S. Singh, and P. C. Srivastava, Ed., World Scientific, Singapore, 1992.
K. Motogami, M. Kono, S. Mori, M. Watanabe, and N. Ogata, Electrochim. Acta, 37, 1725 (1992).
M. Kono, K. Furuta, S. Mori, M. Watanabe, and N. Ogata, Polym. Adv. Technol., 4, 85 (1993).
L. C. Dickinson, P. Morganelli, C. W. Chu, Z. Petroviz, W. J. MacKnight, and J. C. W. Chien, Macromolecules, 21, 338 (1988).
L. C. Dickinson, J. C. W. Chien, and W. J. MacKnight, Macromolecules, 23, 1279 (1990).
K. Ichikawa and W. J. MacKnight, Polymer, 33, 4693 (1992).
K. Ichikawa, L. C. Dickinson, W. J. MacKnight, M. Watanabe, and N. Ogata, Polymer, 33, 4699 (1992).
K. Ichikawa and W. J. MacKnight, Electrochim. Acta, 37, 1511 (1992).
S. Yoon, K. Ichikawa, W. J. MacKnight, and S. L. Hsu, Macromolecules, 28, 5063 (1995).
N. G. McCrum, B. E. Read, and G. Williams, “Anelastic and Dielectric Effects in Polymeric Solids,” Wiley, New York, N.Y., 1969.
M. L. Williams, R. F. Landel, and J. D. Ferry, J. Am. Chem. Soc., 77, 3701 (1955).
R. H. Cole and K. S. Cole, J. Chem. Phys., 9, 341 (1941).
A. L. McClellan, “Tables of Experimental Dipole Moments,” W. H. Freeman, San Francisco, 1963.
A. H. Price, in “Dielectric and Molecular Behaviour,” N. E. Hill, W. H. Vaughan, A. H. Price, and M. Davis, Ed., Van Nostrand Reinhold, New York, N.Y., 1969.
A. A. Jones in “High Resolution NMR Spectroscopy of Synthetic Polymers in Bulk,” R. A. Komoroski, Ed., VCH, Derfield Beach, Florida, 1986.
J.-F. Shi, L. C. Dickinson, W. J. MacKnight, and J. C. W. Chen, Macromolecules, 26, 5908 (1993).
C. H. Roland, Macromolecules, 27, 4242 (1994).
L. Lestel, P. Guegan, S. Boileau, H. Vheradame, and F. Laupretre, Macromolecules, 25, 6024 (1992).
M. Muller, R. Stadler, F. Kremer, and G. Williams, Macromolecules, 28, 6942 (1995).
P. A. Beckmann, Phys. Rep., 171, 85 (1988).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ichikawa, K., Dickinson, L., MacKnight, W. et al. Molecular Relaxations of a Branched Poly(oxyethylene) Network Polymer. Polym J 29, 429–433 (1997). https://doi.org/10.1295/polymj.29.429
Issue date:
DOI: https://doi.org/10.1295/polymj.29.429