Table 1 Photovoltaic parameters for all-PSCs based on PBTA-Si:PTzBI-Si:N2200 (1.3:0.7:1)

From: Surpassing the 10% efficiency milestone for 1-cm2 all-polymer solar cells

Area (cm2)

Thickness (nm)

Solvent additive

VOC (V)

JSC, EQEd (mA cm−2)

FF (%)

PCEf (%)

0.05a

130

/

0.85

14.24

75.3

9.1

 

320

/

0.83

16.30

64.6

8.7

0.05a

130

DBEc

0.83

14.07

80.0

9.3

 

380

DBEc

0.82

17.52

72.1

10.4

1.0b

130

DBEc

0.85

15.05e

76.3

9.8

 

350

DBEc

0.84

17.76e

66.8

10.0

  1. The errors are defined as the standard deviation
  2. aAperture with an area of 0.04 cm2 was used
  3. bAperture with an area of 0.9062 cm2 was used
  4. cThe volume ratio of DBE is 0.1%
  5. dJSC, EQE is defined as the calculated current density from EQE spectra
  6. eThe average of current densities obtained from EQEs with light-spots concentrating on three locations of 1.0 cm2-cell
  7. fThe efficiency is calculated by, PCE = VOC·JSC, EQE·FF