Fig. 3: The structural evolution of the Ce65Al10Co25 HOS sample under high-pressure.
From: Two-way tuning of structural order in metallic glasses
a S(q) and b G(r) of the HOS sample during compression, c S(q), and d G(r) of the HOS sample during decompression. Fewer features in the S(q) and G(r) after high-pressure treatment indicate that thermal-driven high orderings are gradually erased by pressure. A comparison of the structures of the as-prepared sample (LOS) and the sample recovered from high-pressure experiments (HP-LOS) is shown in e S(q) and f G(r). The HP-LOS sample (blue line) almost coincides with the as-prepared LOS MG (red circle), suggesting highly similar structures.