Table 1 Photovoltaic parameters of the OPVs based on PM6:NFA blends.

From: Unveiling structure-performance relationships from multi-scales in non-fullerene organic photovoltaics

Blenda

Voc

(V)

Jsc

(mA cm−2)

FF

(%)

PCE

(%)b

Jcal.

(mA cm−2)c

μh

(10−4 cm2 V−1 s−1)d

μe

(10−4 cm2 V−1 s−1)e

PM6:BO-4Cl

0.845 (0.846 ± 0.002)

26.70 (26.62 ± 0.13)

75.83 (75.20 ± 0.53)

17.21 (17.02 ± 0.15)

26.39

2.50 ± 0.62

2.76 ± 0.83

PM6:BTP-S7

0.861 (0.859 ± 0.003)

25.92 (26.00 ± 0.12)

75.09 (73.62 ± 0.59)

16.76 (16.51 ± 0.16)

25.87

2.29 ± 0.35

3.28 ± 0.70

PM6:BTP-S8

0.852 (0.852 ± 0.002)

26.96 (26.66 ± 0.36)

75.45 (74.99 ± 1.05)

17.33 (17.05 ± 0.11)

26.56

2.27 ± 0.30

4.27 ± 1.34

PM6:BTP-S9

0.846 (0.848 ± 0.003)

26.47 (26.48 ± 0.14)

78.44 (77.72 ± 0.46)

17.56 (17.42 ± 0.07)

26.42

2.40 ± 0.20

4.68 ± 0.20

  1. aActive area: 9.25 mm2, measured with a mask (area: 5.979 mm2, certified).
  2. bValues in the parentheses are the average PCEs based on ten devices.
  3. cCalculated current densities from the corresponding EQE curves.
  4. dHole mobilities measured via the SCLC method.
  5. eElectron mobilities measured via the SCLC method.