Fig. 2: EBSD inverse pole figure (IPF)+ image quality (IQ) maps of Ti-O and Ti-Al-O alloys after tensile fracture in liquid nitrogen.
From: Elimination of oxygen sensitivity in α-titanium by substitutional alloying with Al
The fracture strain was also indicated in each microstructure. When the oxygen content is 0.1 wt%, the deformation twinning was basically suppressed with 4wt.% of aluminum addition, whereas when the oxygen content is 0.3 wt%, the deformation twinning was basically suppressed with 2wt.% of aluminum addition. The scale bar applies to all panels in this figure.