Fig. 7: Ex situ SEM postmortem morphological investigations of the bare Cu, AO and BTO scaffold after plating to 1 mA h cm−2 at a current density of 2 mA cm−2. | Nature Communications

Fig. 7: Ex situ SEM postmortem morphological investigations of the bare Cu, AO and BTO scaffold after plating to 1 mA h cm−2 at a current density of 2 mA cm−2.

From: High dielectric barium titanate porous scaffold for efficient Li metal cycling in anode-free cells

Fig. 7

a, b Bare copper electrode and zoomed-in figure, c, d BTO scaffold and zoomed-in figure, e, f AO scaffold and zoomed-in figure, g, h cross-section of BTO and Cu electrode after depositing 1 mA h cm−2 Li metal at a current density of 2 mA cm−2. Insets show the digital images of the complete electrodes.