Fig. 3: The temperature dependence of MR at Fe0.29TaS2/SC interface. | Nature Communications

Fig. 3: The temperature dependence of MR at Fe0.29TaS2/SC interface.

From: Evidence for anisotropic spin-triplet Andreev reflection at the 2D van der Waals ferromagnet/superconductor interface

Fig. 3

a The interfacial resistance as a function of \(\Theta\)yz measured on device B at T = 2 K (blue), 4 K (yellow) 8 K (olive), and 9 K (black), respectively. These results were obtained under B = 5 T and Vbias = 1 mV, which correspond to V3T ~ 0.40 mV for T = 2 and 4 K, and V3T ~ 0.25 mV for T = 8 and 9 K. b The temperature dependence of MR ratio of device B at B = 9 T, 7 T, and 5 T, respectively. The error bars correspond to one standard deviation. The open circles represent the absence of obvious MR.