Fig. 6: Material properties. | Nature Communications

Fig. 6: Material properties.

From: Precise cooperative sulfur placement leads to semi-crystallinity and selective depolymerisability in CS2/oxetane copolymers

Fig. 6

a DSC curve of the 2nd heating cycle for polymer corresponding to Table 1, run #1. b Overlay plots of storage modulus E’, loss modulus E” and tan(E”/E’) for hot-pressed films (example photograph inlayed) with materials from Table 1 run #9 measured by DMA (tension film mode, 1 Hz, 1 °C per min). c Free energy release upon association of model oligomers assessed on the B3LYP/cc-pVDZ level of theory.