Fig. 2: Vitrification behavior of metallic glasses with different sizes.
Specific heat scans at heating rates, qh, after cooling at the indicated rates, qc, for Au49Cu26.9Si16.3Ag5.5Pd2.3 at.% with leq = 5.7 μm (a) and 0.9 μm (b), as well as for Pt57.5Cu14.7Ni5.3P22.5 at.% with leq = 10.8 μm (c) and 1.3 μm (d). The gray lines are linear fits of the glass and the melt-specific heat and coincide with those reported in the inset of Fig. 1.