Fig. 1: Synthesis and microstructure characterization of phosphor-glass composites.
From: Rapid synthesis of phosphor-glass composites in seconds based on particle self-stabilization
a Model on temperature-time profile of fast synthesis process. b Optical and fluorescence photograph of YAG:Ce-PGC (phosphor content: 10 wt% and also used hereafter.), flat discs sample (diameter of 2.2 cm and thickness of 1.0 mm, scale bar, 1 cm). c Optical microscope image of YAG:Ce-PGC (scale bar, 200 μm), inset is enlarged image (scale bar, 50 μm). d Transmission spectra of YAG:Ce-PGC 10 wt% and tellurite glass. e Comparison of YAG:Ce particle size before and after composite. f Surface and 3D reconstruction CLSM image of YAG:Ce-PGC (scale bar, 200 μm). g HAADF-STEM image and corresponding EDS mappings profiles across the interface between YAG:Ce crystal and tellurite glass (scale bar, 50 nm). Source data are provided as a Source Data file.