Fig. 2: NPPOC-TMG in DCPD resins.
From: Active light-controlled frontal ring-opening metathesis polymerization
a Front velocity (vf) and polymerization enthalpy (Hrxn) with standard deviations for unirradiated FROMP resins with varied mol eq. NPPOC-TMG: catalyst, demonstrating a small decrease in vf with increasing NPPOC-TMG loading but no statistically significant impact on Hrxn (Supplementary Table S1 and Figures S6–S8). b NPPOC-TMG conversion in DCPD measured by NMR spectroscopy when 1.3 mm thick samples are exposed to 365 nm and 385 nm light for varied preirradiation times.