Fig. 1
From: Closing the gap between atomic-scale lattice deformations and continuum elasticity
Dislocations and strain field in 2D for a crystal having triangular symmetry. a A2 (left) and n (right), showing a schematics of the position and orientation of defects, as well as atomic planes at and close to one defect. b Magnification of n and Burgers vector. c εxx as computed from ηj. Comparison between results from APFC (black circles) and from continuum elasticity (CE) (solid red line) along specific directions as in panel (c) are shown: (d) εxx along \(\ell _1\), (e) εxx along \(\ell _2\), (f) εyy along \(\ell _1\), (g) εxy along \(\ell _3\)
