Fig. 1: Yield strength maps at 1300 K. | npj Computational Materials

Fig. 1: Yield strength maps at 1300 K.

From: Computational discovery of ultra-strong, stable, and lightweight refractory multi-principal element alloys. Part II: comprehensive ternary design and validation

Fig. 1

Ternary yield strength maps in composition space for the ternary systems a Cr-Ta-W and b Cr-Nb-W at 1300 K. The black dot is the maximum YS in the system (Cr-Ta-W: 2.03 GPa, Cr-Nb-W: 1.87 GPa), the black dashed line is 0.1 GPa from the maximum, and the gray solid lines are 0.1 GPa increments. The semi-transparent gray overlay indicates regions with BCC phase fraction <100%.