Table 1 The nominal composition of 32 Ames Lab combinatorial arc-melted samples (AL) A1–A8, B1–B8, C1–C8, and D1–D8, along with DFT universal strength metric rs and Young’s moduli E.
From: Design of refractory multi-principal-element alloys for high-temperature applications
ID | Nominal composition (at.%) | rs | E | ID | Nominal composition (at.%) | rs | E | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Mo | W | Ta | Ti | Zr | Al | Cr | Mo | W | Ta | Ti | Zr | Al | Cr | ||||||
ALA1 | 85 | 0 | 10 | 2.5 | 2.5 | 0 | 0 | 1.822 | 257.6 | ALC1 | 80 | 0 | 10 | 5 | 5 | 0 | 0 | 1.837 | 237.1 |
ALA2 | 83.3 | 1.7 | 10 | 2.5 | 2.5 | 0 | 0 | 1.821 | 260.0 | ALC2 | 78.4 | 1.6 | 10 | 5 | 5 | 0 | 0 | 1.836 | 246.3 |
ALA3 | 80.8 | 4.3 | 10 | 2.5 | 2.5 | 0 | 0 | 1.819 | 256.3 | ALC3 | 76 | 4 | 10 | 5 | 5 | 0 | 0 | 1.835 | 249.7 |
ALA4 | 78.2 | 6.8 | 10 | 2.5 | 2.5 | 0 | 0 | 1.818 | 264.7 | ALC4 | 73.6 | 6.4 | 10 | 5 | 5 | 0 | 0 | 1.833 | 247.3 |
ALA5 | 76.5 | 8.5 | 10 | 2.5 | 2.5 | 0 | 0 | 1.817 | 268.9 | ALC5 | 72 | 8 | 10 | 5 | 5 | 0 | 0 | 1.832 | 240.1 |
ALA6 | 72.3 | 12.8 | 10 | 2.5 | 2.5 | 0 | 0 | 1.814 | 273.7 | ALC6 | 68 | 12 | 10 | 5 | 5 | 0 | 0 | 1.83 | 241.0 |
ALA7 | 80.8 | 4.3 | 5 | 2.5 | 2.5 | 5 | 0 | 1.83 | 261.2 | ALC7 | 76 | 4 | 5 | 5 | 5 | 5 | 0 | 1.846 | 240.4 |
ALA8 | 80.8 | 4.3 | 5 | 2.5 | 2.5 | 0 | 5 | 1.813 | 272.2 | ALC8 | 76 | 4 | 5 | 5 | 5 | 0 | 5 | 1.828 | 243.6 |
ALB1 | 80 | 0 | 12.5 | 3.8 | 3.8 | 0 | 0 | 1.831 | 243.9 | ALD1 | 80 | 0 | 20 | 0 | 0 | 0 | 0 | 1.812 | 260.1 |
ALB2 | 78.4 | 1.6 | 12.5 | 3.8 | 3.8 | 0 | 0 | 1.83 | 237.6 | ALD2 | 78.4 | 1.6 | 20 | 0 | 0 | 0 | 0 | 1.811 | 266.1 |
ALB3 | 76 | 4 | 12.5 | 3.8 | 3.8 | 0 | 0 | 1.828 | 240.0 | ALD3 | 76 | 4 | 20 | 0 | 0 | 0 | 0 | 1.81 | 267.1 |
ALB4 | 73.6 | 6.4 | 12.5 | 3.8 | 3.8 | 0 | 0 | 1.827 | 250.3 | ALD4 | 73.6 | 6.4 | 20 | 0 | 0 | 0 | 0 | 1.808 | 270.8 |
ALB5 | 72 | 8 | 12.5 | 3.8 | 3.8 | 0 | 0 | 1.826 | 238.4 | ALD5 | 72 | 8 | 20 | 0 | 0 | 0 | 0 | 1.807 | 255.8 |
ALB6 | 68 | 12 | 12.5 | 3.8 | 3.8 | 0 | 0 | 1.824 | 265.8 | ALD6 | 68 | 12 | 20 | 0 | 0 | 0 | 0 | 1.805 | 270.4 |
ALB7 | 76 | 4 | 7.5 | 3.8 | 3.8 | 5 | 0 | 1.84 | 241.1 | ALD7 | 76 | 4 | 15 | 0 | 0 | 5 | 0 | 1.821 | 265.3 |
ALB8 | 76 | 4 | 7.5 | 3.8 | 3.8 | 0 | 5 | 1.822 | 257.4 | ALD8 | 76 | 4 | 15 | 0 | 0 | 0 | 5 | 1.803 | 272.8 |