Table 2 Density and compressive (RT and 1300 °C) properties for AL-A3, A6, A8, Mo NbTaW, HfMoNbTaTi, HfMoNbTaZr, and HfMoTaTiZr.
From: Design of refractory multi-principal-element alloys for high-temperature applications
Room temperature | 1300 °C | |||||
|---|---|---|---|---|---|---|
Sample | Density (g cm−3) | 0.2% YS (MPa) | Specific 0.2% YS (MPa cm3 g−1) | Total strain (%) | 0.2% YS (MPa) | Specific 0.2% YS (MPa cm3 g−1) |
AL-A3 | 11.4 | 820 | 71.9 | 10.0 | ||
AL-A6 | 11.8 | 760 | 64.4 | 9.2 | 446 | 37.8 |
AL-A8 | 10.5 | 750 | 71.4 | 7.8 | ||
MoNbTaW | 13.7 | 1010 | 73.9 | 2.8 | 460 | 33.6 |
HfMoNbTaTi | 10.8 | 1369 | 126.8 | 27 | 530 | 49.1 |
HfMoNbTaZr | 10.9 | 1524 | 139.8 | 16 | 485 | 44.5 |
HfMoTaTiZr | 10.2 | 1600 | 156.9 | 4 | 175 | 17.2 |