Fig. 10: The change of [BO3]-related structure with square root of leaching time, the inset plot is a typical three peak Gaussian fitting for the [BO3] unit ranging from 1250 to 1550 cm−1. | npj Materials Degradation

Fig. 10: The change of [BO3]-related structure with square root of leaching time, the inset plot is a typical three peak Gaussian fitting for the [BO3] unit ranging from 1250 to 1550 cm−1.

From: Influence of radiation on borosilicate glass leaching behaviors

Fig. 10

The dot lines represent the linear region for irradiated sample and dashed lines for un-irradiated samples. For Pristine glass, the surface [BO3] leached out linearly with the increase of the square root of leaching time. After ion irradiation, the loss of [BO3] had been significantly accelerated.