Fig. 10: SEM images of cross-section of QHXC-1 glaze layer.
From: The corrosion mechanism of lead-glazed pottery in Han dynasty
a Glaze cross-section crack. b Corrosion in the shape of clusters of flowers. c Corrosion in the shape of lamella petals.
Fig. 10: SEM images of cross-section of QHXC-1 glaze layer. | npj Materials Degradation