Fig. 16: Schematic of sample exposure for SVET experiments.

(A) For surface corrosion experiments a square area of 6 mm x 6 mm and (B) for cut-edge corrosion experiments a rectangular cross-sectional area of 3 mm x 10 mm was exposed to 0.17 M NaCl pH 7 solution.