Fig. 16
From: Effect of salt deposition patterns on stress corrosion cracking
An optical image showing the crack surface morphology upon complete failure of the CMSX-4 fatigue specimen after 1505 cycles.
Fig. 16 | npj Materials Degradation
From: Effect of salt deposition patterns on stress corrosion cracking
An optical image showing the crack surface morphology upon complete failure of the CMSX-4 fatigue specimen after 1505 cycles.