Fig. 3: Thermal and mechanical characterization of PS82-co-PHCBI18 and PS.
From: Mechanically triggered on-demand degradation of polymers synthesized by radical polymerizations
a, TGA showing a slightly lower Td of the co-polymer compared with the PS homopolymer. b, DSC showing the same glass transition temperature for the co-polymer and the PS homopolymer. c, DMA showing that the storage modulus E′ and the ratio of loss and storage moduli (tan δ), which corresponds to the glass transition temperature are similar for this co-polymer and the PS homopolymer.