Extended Data Fig. 10: Temperature-dependendent magnetization curves of sample 7 (S7) under various pressures under a magnetic field applied perpendicular to the ab plane using the zero-field-cooled (ZFC) and field-cooled (FC) modes.
From: Superconductivity in pressurized trilayer La4Ni3O10−δ single crystals
a, 2.0 GPa and10 Oe b, 2.0 GPa 20 Oe. Temperature dependent magnetization curves at 5.0 GPa under magnetic fields of c, 5.0 GPa and 20 Oe and d, 5.0 GPa and 50 Oe. e, 15.0 GPa and 5 Oe; f, 15.0 GPa and 20 Oe; g, 15.0 GPa and 50 Oe; h, 15.0 GPa and 100 Oe. i, 30.0 GPa and 5 Oe; j, 30.0 GPa and 20 Oe; k, 30.0 GPa and 50 Oe; l, 30.0 GPa and 100 Oe. m, 49.0 GPa and 5 Oe; n, 49.0 GPa and 10 Oe; o, 49.0 GPa and 20 Oe; p, 49.0 GPa and 100 Oe. The inset shows the photo of the crystal in the mini-DAC.