Fig. 2: Macroscopic assessment of material properties.
From: A ductile chromium–molybdenum alloy resistant to high-temperature oxidation
a, Area-specific mass change during cyclic oxidation at 800 °C (left) and 1,100 °C (right). b, Representative true stress–true strain curves obtained from compression tests conducted at RT and 900 °C. c, One per cent offset yield strength as a function of temperature. d, True work hardening as a function of true stress. At least two samples per test temperature were tested and uncertainty was estimated using the standard deviations.