From: Origin of abnormal structural transformation in a (BiPb)FeO3/SrRuO3/SrTiO3 hetero-structure probed by Rutherford backscattering

Figure 2

Random and aligned RBS spectra for (BiPb)FeO3/SrRuO3/SrTiO3 heterostructures. Random (red) and aligned RBS spectra (along [001] direction) (black) for (BiPb)FeO3/SrRuO3/SrTiO3 heterostructures. RBS ratio (χ min : 34 to 100%) (blue triangle) at (BiPb)FeO3 surfaces clearly indicates crystalline quality degradation and eventually completes an overlap of aligned to random spectra at high T g . Inset shows RBS experimental sketch.