Table 1 Room-temperature tensile properties of the twin-roll-cast Ti/Al clad specimens.
From: Novel twin-roll-cast Ti/Al clad sheets with excellent tensile properties
Clad Specimen | Yield Strength (MPa) | Tensile Strength (MPa) | Total Elongation (%) | Strain at Cracking (%) | Strain at Interfacial Delamination (%) |
|---|---|---|---|---|---|
As Cast | 99 ± 5 | 152 ± 7 | 17.0 ± 1.2 | 7.8 ± 1.3 * | 12.5 ± 0.8 |
TA33 | 116 ± 7 | 212 ± 5 | 36.0 ± 2.9 | 21.6 ± 4.4 * | 31.3 ± 1.0 |
TA36 | 120 ± 4 | 217 ± 8 | 54.5 ± 2.2 | 43.4 ± 3.4 * | 51.4 ± 3.3 |
TA41 | 118 ± 7 | 211 ± 7 | 41.1 ± 0.8 | — | 30.6 ± 0.8 * |
TA43 | 132 ± 5 | 218 ± 9 | 46.1 ± 1.8 | — | 40.5 ± 1.5 * |
TA46 | 123 ± 4 | 213 ± 6 | 44.3 ± 2.5 | 24.5 ± 2.2 * | 27.6 ± 1.7 |
TA51 | 115 ± 3 | 227 ± 2 | 35.0 ± 1.3 | 27.4 ± 2.9 * | 32.0 ± 1.2 |
TA53 | 118 ± 2 | 229 ± 4 | 44.5 ± 1.7 | — | 29.2 ± 3.3 * |
TA56 | 115 ± 3 | 221 ± 2 | 50.7 ± 2.2 | — | 30.7 ± 2.0 * |
TA61 | 91 ± 3 | 214 ± 5 | 48.8 ± 1.1 | — | 27.9 ± 1.1 * |
TA63 | 83 ± 3 | 198 ± 3 | 17.4 ± 2.1 | — | 17.2 ± 0.5 * |
H32-treated | 151 ± 4 | 234 ± 6 | 38.4 ± 3.3 | — | 28.8 ± 2.8 * |