Figure 6 | Scientific Reports

Figure 6

From: Atomic-scale engineering of ferroelectric-ferromagnetic interfaces of epitaxial perovskite films for functional properties

Figure 6

Magnetization measurements of S5, S1 and S2. (a) Hysteresis loop measurements at 10 K after field cooling (FC = 10 kOe) and measured along the [100] and [110] directions for the sample S5. The ZFC curve measured along the [100] direction is also shown for comparison. (b) Hysteresis loop measurements at 10 K for the sample S1 after field cooling and measured along the [100] and [110] directions and S2 after field cooling and measured along the [001] direction.