Figure 2 | Scientific Reports

Figure 2

From: Design and Synthesis of an Artificial Perpendicular Hard Ferrimagnet with High Thermal and Magnetic Field Stabilities

Figure 2

Magnetic properties of [MnGa (t nm)/Co2MnSi]5 superlattices. (Sample A: t = 3.75 nm, red circles; sample B: t = 4.5 nm, black squares; sample C: t = 5.6 nm, blue up triangles). (a) Net magnetization (M net) versus temperature (T) for samples A, B and C from 50 to 350 K. (b) Hystereses of samples A, B and C measured in a magnetic field range from −50 to +50 kOe at 280 K.