Figure 5 | Scientific Reports

Figure 5

From: Electrochemical Production of Glycolic Acid from Oxalic Acid Using a Polymer Electrolyte Alcohol Electrosynthesis Cell Containing a Porous TiO2 Catalyst

Figure 5

(a) OX conversions, (b) Faradaic efficiency, and (c) current density during the operation of the PEAEC equipped with TiO2/Ti-F cathode (OX concentration: 1 M, reaction area: 25 cm2, flow rate: 0.1 ml min–1, IrO2: 10 mg cm–2, temperature: 60 °C). Inset shows averaged current density (I av) at each applied voltage.