Table 5 Average Compositions of V(C,N) and M6C-Type Carbides in M42 HSS after Annealing.

From: Influence of the Nitrogen Content on the Carbide Transformation of AISI M42 High-Speed Steels during Annealing

V(C,N) + M6C

Element (mass%)

Fe

Cr

Co

Mo

W

V

N

Σ

M42

3.381

0.764

0.536

5.501

1.331

0.987

0.005

12.505

M42-N

4.394

0.843

0.659

8.694

1.401

0.998

0.011

17.000