Table 2 The number and fraction of the remaining displaced atoms after a 5 ns defect evolution of FCC CoCrFeMnNi HEA, pure Ni and pure BCC Fe samples containing randomly distributed initial defects of 1%, averaged from four simulations at 773 K.
From: Origin of radiation resistance in multi-principal element alloys
Alloy | Number of remaining displaced atoms (stdev) | Fraction of remaining displaced atoms (stdev) |
|---|---|---|
CoCrFeMnNi HEA | 85.3 (12.1) | 0.27 (0.04) |
Pure FCC Ni | 167.3 (56.1) | 0.52 (0.18) |
Pure BCC Fe | 87 (1.4) | 0.54 (0.01) |