Table 1 A comparison of the lattice planar spacing (dhkl) obtained from XRD and SAED pattern of BaZr1-xHoxO3-δ ceramics for x = 0.05, 0.10, 0.15, and 0.20 calcined at 1100 °C for 4 h in air.
x | Lattice constant obtained from XRD Pattern (nm) | Lattice plane (hkl) | Lattice planar spacing (dhkl) obtained from XRD pattern (nm) | Lattice planar spacing (dhkl) obtained from SAED pattern (nm) |
|---|---|---|---|---|
0.05 | 4.1981 | 110 | 0.2958 | 0.2946 |
0.10 | 4.2021 | 111 | 0.2326 | 0.2345 |
0.15 | 4.2052 | 110 | 0.2971 | 0.2988 |
0.20 | 4.2068 | 100 | 0.4233 | 0.4253 |