Table 2 List of samples used, including material and temperature treatment applied. For details of the used methods see section II C.
From: Vacancy-Hydrogen Interaction in Niobium during Low-Temperature Baking
Sample | Material | Method | Facility | Treatment |
|---|---|---|---|---|
6 | Ningxia | PALS, CDB | Prague | 70 °C for 4 h, 120 °C for 4, 40, 180 h in \({\rm{p}}\,\le \,{10}^{-3}\,{\rm{mbar}}\) |
73 | Tokyo Denkai | PALS, CDB | Prague | 70 °C for 4 h, 120 °C for 4, 40, 180 h in \({\rm{p}}\,\le \,{10}^{-3}\,{\rm{mbar}}\) |
14 | Ningxia | DB-VEPAS | AIDA | DESY sample furnace at 70 °C for 4 h in \({\rm{p}}\,\approx \,{10}^{-6}\,{\rm{mbar}}\) |
17 | Ningxia | DB-VEPAS | AIDA | Steps from 70 °C to 120 °C for 4 h each in \({\rm{p}}\,\approx \,{10}^{-10}\,{\rm{mbar}}\) |
64 | Tokyo Denkai | DB-VEPAS | AIDA | Steps from 70 °C to 120 °C for 4 h each in \({\rm{p}}\,\approx \,{10}^{-10}\,{\rm{mbar}}\) |
78 | Tokyo Denkai | VEPALS | MePS | Steps from 70 °C to 120 °C for 4 h each in \({\rm{p}}\,\le \,{10}^{-7}\,{\rm{mbar}}\) |