Table 3 Fitted composition-dependence of the CL parameters (Eq. 3) in the position range of 0–8 mm (corresponding to \(x=0.0 \ldots 0.4\)) for each sample.
Sample | \(p_H/p = 0\) | \(p_H/p = 0.05\) | \(p_H/p = 0.1\) | \(p_H/p = 0.2\) | From Ref.54 |
|---|---|---|---|---|---|
Parameter | \(\mathbf {(p_1,p_2,p_3)}\) parameters for \(\mathbf {y=p_1\cdot x^2+p_2\cdot x+p_3}\), \(\hbox {R}^2\) | ||||
A (eV) | (14.03,-37.7, 117.46), 0.97 | (6.73, -11.69, 95.58), 0.98 | (30.26, -44.89, 103.50), 0.97 | (27.13, -46.89, 107.86), 0.99 | (18.4, -42.5, 92.9), 0.74 |
\(\Gamma \) (eV) | (− 0.02, 0.53, 2.70), 0.99 | (0.03, 0.40, 2.94), 0.99 | (− 0.04, 0.52, 3.02), 0.99 | (− 0.25, 0.92, 2.86), 0.99 | (− 2.33, 2.26, 2.54), 0.97 |
\(\hbox {E}_0\) (eV) | (− 0.12, 0.33, 3.68), 0.99 | (− 0.03, 9, 52*, 3.72), 0.84 | (− 0.22, 0.30, 3.73), 0.96 | (− 0.24, 0.41, 3.63), 0.98 | − |
\(\hbox {E}_g^{CL}\) (eV) | (0.06, − 0.14, 0.944), 0.85 | (0.05, − 0.21, 1.15), 0.98 | (− 0.03, − 0.15, 1.33), 0.99 | (− 0.06, − 0.16, 1.43), 0.99 | (0.08, − 1.09, 1.70), 0.99 |
\(\hbox {E}_p\) (eV) | (0.22, − 1.16, 1.99), 0.98 | (0.13, − 0.49, 1.33), 0.99 | (0.70, − 1.35, 1.61), 0.99 | (0.63, − 1.39, 1.81), 0.99 | (0.33, − 2.01, 1.35), 0.96 |