Figure 6 | Scientific Reports

Figure 6

From: In-situ neutron diffraction study of lattice deformation behaviour of commercially pure titanium at cryogenic temperature

Figure 6

Evolution of lattice strains as a function of applied stress at 15–298 K for (a) RD and (b) TD loading directions. The sections of microyielding in {hkil} grain families (grey-region) are magnified, and the same axial ranges are given to these magnified graphs with 6 micro strains in x-axes and 400 MPa in y-axes. The data deviation is quite small less than 0.3 (not shown in the figure).