Table 1 The six ab initio melting points of bcc-Cr, \((P_m,\,T_m\pm \Delta T_m),\) obtained from the Z method implemented with VASP.
Lattice constant (Å) | \(P_m\) (GPa) | \(T_m\) (K) | \(\Delta \) \(T_m\) (K) |
|---|---|---|---|
3.00 | \(-\) 5.2 | 1950 | 62.5 |
2.80 | 47.9 | 3330 | 125.0 |
2.65 | 124 | 4460 | 187.5 |
2.50 | 266 | 5840 | 187.5 |
2.35 | 526 | 7720 | 250.0 |
2.25 | 815 | 9310 | 250.0 |