Figure 3 | Scientific Reports

Figure 3

From: Analysis of the carbide precipitation and microstructural evolution in HCCI as a function of the heating rate and destabilization temperature

Figure 3

IPF + IQ and Phase + IQ maps corresponding to the samples heated at two heating rates up to the three analysed destabilization temperature. Larger transformed areas are observed in samples slow heated. Consider that EBSD maps might fail in the quantification of RA, due to low statistic and possible austenite to martensite transformation during preparation.