Figure 2
From: Explaining the entropy forming ability for carbides with the effective atomic size mismatch
(a) The different multinary level alloys all show the same correlation between EFA and \(\sigma _1\). The lines represent power law fits as in Fig. 1a for every multinary level. Note, that the scaling of EFA is different for every multinary level. (b) The correlation between \(\delta\) and \(\sigma _1\) is also apparent at all multinary levels. Note, that at large values of \(\delta\), the lattice distortion \(\sigma _1\) is always significant.