Table 1 Summary of experimental test matrix. The time to rupture does not include the soaking time (0.5 h).
Sample | T [°C] | Nominal stress [MPa] | Minimum strain rate [s−1] | Time to rupture [h] |
|---|---|---|---|---|
VLE1 | 482 | 455 | 1.0 × 10–9 | n.a. |
545 | 9.5 × 10–9 | n.a. | ||
VLE2 | 554 | 7.0 × 10–8 | n.a. | |
600 | 3.0 × 10–7 | n.a. | ||
VLE3 | 540 | 2.0 × 10–9 | n.a. | |
660 | 4.5 × 10–7 | n.a. | ||
CLE1 | 548 | 1.6 × 10–8 | 447 | |
CLE2 | 550 | 8.1 × 10–8 | 161 | |
CLE3 | 568 | 3.0 × 10–7 | 45 | |
CLE4 | 600 | 5.6 × 10–7 | 21 | |
CLE5 | 660 | 9.0 × 10–6 | 0.7 | |
CLE6 | 700 | 3.6 × 10–5 | 0.2 | |
VLE4 | 427 | 671 | 1.6 × 10–9 | n.a. |
VLE4 | 756 | 7.0 × 10–8 | n.a. | |
CLE7 | 675 | 6.8 × 10–9 | interr. 600 | |
CLE8 | 678 | 2.6 × 10–7 | 49 | |
CLE9 | 700 | 5.3 × 10–7 | 24 | |
CLE10 | 710 | 3.9 × 10–6 | 3.8 | |
CLE11 | 725 | 6.0 × 10–6 | 2.6 |