Table 2 Shows the aspect ratios of the grains, at each figure, at a certain frequency, the critical threshold and the Dielectric constant peak.
Aspect ratio | Critical threshold | Case | Dielectric constant peak | Frequency | Figure |
|---|---|---|---|---|---|
27:1 | 1.8 | Conductor in insulator at the same direction of the current | 108.96 | 100 Hz | Figure 3 |
9:1 | 8.9 | 324.92 | |||
3:1 | 24.74 | 763.81 | |||
1:1 | 33.33 | 1156.7 | |||
0.333:1 | 26.403 | 898.96 | |||
0.111:1 | 14.12 | 567.04 | |||
0.037:1 | 5.7967 | 337.79 | |||
– | – | No peak | 107 Hz | Figure 4 | |
9:1 | 35.403 | Insulator in insulator at the same direction of the current | 1254.4 | 100 Hz | Figure 5 |
3:1 | 34.458 | 1209.9 | |||
1:1 | 33.33 | 1158.8 | |||
0.333:1 | 36.558 | 1342.7 | |||
0.111:1 | 49.201 | 2150.9 | |||
0.037:1 | 69.026 | 3804.8 | |||
0.012:1 | 85.778 | 6675.2 | |||
0.004:1 | 94.604 | 11,641 | |||
0.001:1 | 98.105 | 20,103 | |||
0.0005:1 | 99.359 | 34,584 | |||
– | – | No peak | 107 Hz | Figure 6 | |
27:1 | 1.8 | Conductor in insulator at the same direction of the current |  | 100 Hz | Figure 7 |
9:1 | 8.9 | ||||
3:1 | 24.74 | ||||
1:1 | 33.33 | ||||
0.333:1 | 26.403 | ||||
0.111:1 | 14.12 | ||||
0.037:1 | 5.7967 | ||||
– | – | No peak | 107 Hz | Figure 8 | |
9:1 | 35.403 | Insulator in insulator at the same direction of the current | 1254.4 | 100 Hz | Figure 9 |
3:1 | 34.458 | 1209.9 | |||
1:1 | 33.33 | 1158.8 | |||
0.333:1 | 36.558 | 1342.7 | |||
0.111:1 | 49.201 | 2150.9 | |||
0.037:1 | 69.026 | 3804.8 | |||
0.012:1 | 85.778 | 6675.2 | |||
0.004:1 | 94.604 | 11,641 | |||
0.001:1 | 98.105 | 20,103 | |||
0.0005:1 | 99.359 | 34,584 | |||
– | – | No peak | 107 Hz | Figure 10 |