Table 3 Best fit parameters obtained from the U-LIII EXAFS fitting results of the Ln and U loaded glass samples.
From: Structural characterization of uranium and lanthanide loaded borosilicate glass matrix
| Â | UVI-Oaxial | UVI-Oequatorial | UV-O | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|  | N(O) | UVI [at%] (x) | R [Å] | DW [×10−3 Å2] | N(O) | R [Å] | DW [×10−3 Å2] | N(O) | UV [at%] (1-x) | R [Å] | DW[×10−3 Å2] |
MUCe | 2 × x | 75 ± 6 | 1.85 ± 0.01 | 1.5 | 6 × x | 2.30 ± 0.03 | 14.8 | 6 × (1-x) | 25 ± 6 | 2.20 ± 0.02 | 2.4 |
MUNd | 2 × x | 65 ± 8 | 1.83 ± 0.01 | 1.5 | 6 × x | 2.29 ± 0.03 | 13.6 | 6 × (1-x) | 35 ± 8 | 2.20 ± 0.02 | 3.1 |
MUEu | 2 × x | 63 ± 6 | 1.85 ± 0.01 | 2.3 | 6 × x | 2.28 ± 0.03 | 13.2 | 6 × (1-x) | 37 ± 6 | 2.18 ± 0.02 | 1.7 |
MUCNE | 2 × x | 73 ± 7 | 1.84 ± 0.01 | 1.4 | 6 × x | 2.28 ± 0.03 | 13.8 | 6 × (1-x) | 27 ± 7 | 2.20 ± 0.02 | 1.5 |