Fig. 2: Magnetisation data for the samples 31Cr and 31NCr.
From: Controlling spin pumping into superconducting Nb by proximity-induced spin-triplet Cooper pairs
a Magnetic field dependent magnetisation curves M(H) for film 31Cr in four orientations with respect to the applied in-plane field measured at 300 K. b Ferromagnetic resonance (FMR) absorption power derivative (\({{{{{\rm{d}}}}}}P/{{{{{\rm{d}}}}}}H\)) for sample 31Cr measured at 16 K. c Resonance magnetic field μ0Hres as a function of temperature for film 31Cr and 31NCr extracted from FMR measurements. d The temperature dependence of the difference in μ0Hres between the hard and easy orientations (\({\mu }_{0}\varDelta {H}_{{{{{{\rm{res}}}}}}}\)) for films 31Cr and 31NCr. Errors for the μ0Hres data are from the Lorentzian derivative fitting.