Table 4 Slurry identification table for order of mixing in relation to both silicon nitride powders

From: Rheology improvement for silicon nitride and resin slurries for vat photopolymerization printing and sintering

Slurry ID

Wt.% KD1, order added

Wt.% CC42, order added

1KD1/1CC42

1, before powder

1, after powder

1KD1/2CC42

1, before powder

2, after powder

1KD1/4CC42

1, before powder

4, after powder

2KD1/1CC42

2, before powder

1, after powder

4KD1/1CC42

4, before powder

1, after powder

1CC42/1KD1

1, after powder

1, before powder

1CC42/2KD1

2, after powder

1, before powder

1CC42/4KD1

4, after powder

1, before powder

2CC42/1KD1

1, after powder

2, before powder

4CC42/1KD1

1, after powder

4, before powder

C1KD1/1CC42

1, coated onto powder

1, after powder

C1KD1/2CC42

1, coated onto powder

2, after powder

C1KD1/4CC42

1, coated onto powder

4, after powder

C2KD1/1CC42

2, coated onto powder

1, after powder

C4KD1/1CC42

4, coated onto powder

1, after powder

4CC42

--

4, before powder

4CC42/2BYK103

--

4, before powder

4CC42/2BYK103/1PEG400

--

4, before powder

4CC42/2BYK103/1PG

--

4, before powder

  1. Slurries with Disperbyk 103, PG, and PEG400 all had those constituents added after the entire slurry was made to modify the rheology.