Figure 4
From: Positive exchange-bias and giant vertical hysteretic shift in La0.3Sr0.7FeO3/SrRuO3 bilayers
(a) Coercivity (HC) (closed symbols) and average saturation magnetization (Mav) (open symbols) versus cooling field (HCF) at a temperature of 2 K, (b) Magnetization (M) versus magnetic field (H) loops at different HCF for LSMosaicD, (c) Exchange bias (HEB) with number of cycles (n) [solid line is the fit as per equation. 1] for LSMosaicC and LSNon-mosaic, inset shows vertical shift (Mshift) versus HCF for LSMosaic (LSMosaicA → LSMosaicD) and LSNon-mosaic samples and (d) shows the maximum Mshift (~35%) for the optimized bilayer [LSFO (110 nm)/SRO(10 nm)].