Figure 1
From: Time Invariant Surface Roughness Evolution during Atmospheric Pressure Thin Film Depositions
Monte Carlo growth scheme showing several simulation processes.
Solid on solid aggregation can be seen as a side sticking particle sides downward until reaching the surface. This side sticking would be allowed during ballistic deposition. Additionally, surface diffusion can be seen as a particle hops across the surface reaching a more stable state.