Figure 6 | Scientific Reports

Figure 6

From: Active layers of high-performance lead zirconate titanate at temperatures compatible with silicon nano- and microelectronic devices

Figure 6

Multifunctional nature of the PZT thin film prepared from the Seeded Photosensitive solution at 400 °C.

(a) Variation on the current density produced by an oscillating thermal wave after poling (inset shows the evolution of the pyroelectric coefficient with time). (b) Local piezoelectric response by successive hysteresis loops at different voltages.